904L stainless steel consists of chromium, nickel, molybdenum and copper contents, these elements give type 904L stainless steel excellent properties to resist corrosion in dilute sulfuric acid because of addition of copper, 904L commonly is used in high pressure and corrosion environment where 316L and 317L perform poorly.
904L has high nickel composition with low carbon content, copper alloy adding improve its resistance to corrosion, the “L” in 904L stands for low carbon, it is typical Super Austenitic stainless steel, equivalent grades are DIN 1.4539 and UNS N08904, 904L has better properties than other austenitic stainless steels.
904L is a high-alloy austenitic stainless steel known for its exceptional resistance to corrosion, particularly in harsh environments involving sulfuric acid. It combines high chromium content with nickel, molybdenum, and copper, making it one of the best choices for combating both pitting and general corrosion.
| Grade | Ni | Cr | Mo | Cu | C | Mn | Si | P | S | Fe |
|---|---|---|---|---|---|---|---|---|---|---|
| 904L | 23 – 28 | 19 – 23 | 4 -5 | 1 – 2 | 0.02 | 2 | 1 | 0.045 | 0.035 | Balance |
| Grade | Tensile Strength, Min | Yeild Strength, Min | Elognation | Hardness |
|---|---|---|---|---|
| 904L | 490 Mpa | 215 Mpa | 35% | 90 HRB Max |
| Grade | Density (Kg/M3) |
Elastic Modulus (GPa) |
Mean Co-Eff Of Thermal Expansion (Μm/M/°C) |
Thermal Conductivity (W/M.K) |
Specific Heat 0-100°C (J/Kg.K) |
Elec Resistivity (NΩ.M) |
|||
|---|---|---|---|---|---|---|---|---|---|
| 0-100°C | 0-315°C | 0-538°C | At 20°C | At 500°C | |||||
| 904L | 7900 | 190 | 15 | – | – | 11.5 | – | 500 | 952 |
904L stainless steel price is expensive, due to high amount of molybdenum and nickel content, that leads to grade 904L is replaced by low cost grades, such as 316L, 317L, 2205, 6Mo and super duplex grades.
904L stainless steel sheet is a type of superaustenitic stainless steel that is designed for moderate to high corrosion resistance in a wide range of environments. It is known for its excellent resistance to reducing acids like sulphuric acid and its ability to withstand chlorides in the environment, which helps prevent pitting and crevice corrosion.
Grade 904L stainless steel bar is a non-stabilized austenitic stainless steel with low carbon content. This high-alloy stainless steel contains copper to enhance its resistance to strong reducing acids, such as sulfuric acid. It also exhibits resistance to stress corrosion cracking and crevice corrosion. Grade 904L bar is non-magnetic and offers excellent formability, toughness, and weldability.
Grade 904L bar contains high amounts of costly ingredients, including molybdenum and nickel. Presently, many applications that once utilized grade 904L bar have shifted to lower-cost duplex stainless steel 2205. The properties of flat rolled products in ASTM B625 are described in the following sections. Note that specifications may not be identical for other products such as bar, tube, and pipe.
Discover the superior quality and corrosion resistance of 904L stainless steel bars.
Ceramic lined pipe is made through self-propagating high-temperature synthesis (SHS) technique.
Cast basalt lined steel pipe is composed by lined with cast basalt pipe, outside steel pipe and cement mortar filling between the two layers.
Ceramic tile lined pipes have very uniform coating of specially formulated ceramic material that is affixed to the inner of the pipe.
The material of the rare earth alloy wear-resistant pipe is ZG40CrMnMoNiSiRe, which is also the grade of rare earth alloy steel.
Tubes Erosion Shields are used to protect boiler tubing from the highly erosive effects of high temperatures and pressures thereby greatly extending tube life.
The ASTM A213 T91 seamless tubes are primarily used for boiler, superheater, and heat-exchanger.